Baadhitaanka mikroskoob elektaroonik ah ayaa loo isticmaalay si loo eego jabka daalka iyo falanqaynta habka jabka; Isla mar ahaantaana, tijaabada daalka qaloocinta lafdhabarta ayaa lagu sameeyay shaybaarrada decarburized ee heerkul kala duwan si loo barbardhigo nolosha daalka ee birta tijaabada ah iyo iyada oo aan lahayn decarburization, iyo in la falanqeeyo saameynta decarburization ee waxqabadka daalka ee birta tijaabada. Natiijooyinku waxay muujinayaan in, ay sabab u tahay jiritaanka isku mar ee oxidation iyo decarburization ee geeddi-socodka kululaynta, isdhexgalka u dhexeeya labada, taasoo keentay in dhumucda lakabka si buuxda u decarburized leh koritaanka heerkulku waxay muujinaysaa isbeddel ah ee sii kordhaya ka dibna hoos u dhaco, dhumucda lakabka si buuxda loo jaray ayaa gaadhaya ugu badnaan qiimaha 120 μm at 750 ℃, iyo dhumucda lakabka si buuxda u decarburized gaadho qiimaha ugu yar ee 20 μm at 850 ℃, iyo xadka daal ee birta imtixaanku waa ilaa 760 MPa, iyo Ilaha dildilaaca daalka ee birta tijaabada ah ayaa inta badan Al2O3 ka mid ah kuwa aan biraha ahayn; Dabeecadda decarburization waxay si weyn u yaraynaysaa nolosha daalka ee birta tijaabada, taas oo saameynaysa waxqabadka daalka ee birta tijaabada, lakabka dhumucdiisuna waxay hoos u dhigtaa nolosha daalka. Si loo yareeyo saameynta lakabka decarburization ee waxqabadka daalka ee birta tijaabada, heerkulka daaweynta kulaylka ugu fiican ee birta tijaabada waa in lagu dejiyaa 850 ℃.
Gearku waa qayb muhiim u ah baabuurta,maxaa yeelay qalliinka oo xawaare sare ku socda, qaybta meshing ee dusha marshadu waa inay lahaataa awood sare iyo caabbinta naaxinta, iyo xididka iliggu waa inuu leeyahay daal foorarsi fiican leh sababtoo ah culeyska joogtada ah ee soo noqnoqda, si looga fogaado dildilaaca u horseedaya walxaha. jab. Cilmi-baaristu waxay muujinaysaa in decarburization ay tahay arrin muhiim ah oo saameynaysa lafdhabarta foorarsiga waxqabadka daalka ee alaabta birta ah, iyo foorarsiga waxqabadka daalku waa tilmaame muhiim ah oo tayada badeecada ah, sidaas darteed waxaa lagama maarmaan ah in la barto dabeecadda decarburization iyo qalloocinta waxqabadka daalka ee qalabka tijaabada.
Warqadan, foornada daawaynta kulaylka ee 20CrMnTi gear birta tijaabada decarburization dusha, falanqayn heerkulka kulaylka ee kala duwan ee tijaabada lakabka decarburization qoto dheer ee sharciga beddelka; iyadoo la adeegsanayo QBWP-6000J mashiinka tijaabinta daal fudud ee birta tijaabada ah ee tijaabada daalka foorarsiga rotary, go'aaminta waxqabadka daalka birta tijaabada, isla markaana si loo falanqeeyo saameynta decarburization ee waxqabadka daalka ee birta tijaabada wax soo saarka dhabta ah si loo hagaajiyo habka wax soo saarka, kor loogu qaado tayada alaabta iyo bixiyaan tixraac macquul ah. Tijaabada waxqabadka daalka birta waxaa lagu go'aamiyaa mashiinka tijaabinta daalka qalooca.
1. Qalabka tijaabada iyo hababka
Qalabka tijaabada ah ee cutubka si loo bixiyo 20CrMnTi birta qalabka, iskudhafka kiimikada ugu weyn sida ku cad Shaxda 1. Tijaabada Goynta: Qalabka tijaabada waxaa lagu farsameeyaa muunad cylindrical Ф8 mm × 12 mm, dusha sare waa inuu noqdaa mid dhalaalaya oo aan lahayn wasakh. Foornada daawaynta kulaylka ayaa lagu kululeeyay 675 ℃, 700 ℃, 725 ℃, 750 ℃, 800 ℃, 850 ℃, 900 ℃, 950 ℃, 1,000 ℃, ragga iyo heerkulka hawo -1,000 ℃. Ka dib daaweynta kulaylka ee muunad by dejinta, shiidi iyo polishing, oo leh 4% of nitric acid xal nabaad guurka, isticmaalka mikroskoobyada metallurgical si ay u dhawraan lakabka decarburization steel tijaabada, cabbiraya qoto dheer ee lakabka decarburization heerkulka kala duwan. Tijaabada daalka laablaabashada: walxaha tijaabada ah iyadoo loo eegayo shuruudaha habaynta laba kooxood oo ah noocyada daal laabashada lafdhabarta, kooxda koowaad ma sameeyaan tijaabada decarburization, kooxda labaad ee tijaabada decarburization heerkul kala duwan. Isticmaalka mishiinka tijaabinta daalka qalooca, labada kooxood ee birta tijaabinta qaloocinta tijaabada daalka, go'aaminta xadka daalka ee labada kooxood ee birta tijaabada, isbarbardhigga nolosha daalka ee labada kooxood ee birta tijaabada, adeegsiga iskaanka elektarooniga mikroskoob daal daal indho-indhayn, falanqeeyaan sababaha jabka ee muunad, si ay u sahamiyaan saamaynta decarburization ee sifooyinka daalka ee birta imtixaanka.
Shaxda 1 Halabuurka kiimikaad (jajab tiro) ee birta tijaabada wt%
Saamaynta kuleyliyaha kuleylka ee decarburization
Qaab-dhismeedka ururka decarburization ee hoos yimaada heerkulka kuleylka kala duwan ayaa lagu muujiyay sawirka 1. Sida laga arki karo shaxanka, marka heerkulku yahay 675 ℃, dusha muunada ma muuqato lakabka decarburization; marka heerkulku kor u kaco ilaa 700 ℃, lakabka decarburization dusha muunada ayaa bilaabay inuu u muuqdo, lakabka khafiifka ah ee ferrite; iyadoo heerkulku kor u kaco ilaa 725 ℃, dhumucda lakabka decarburization dusha muunada ayaa si aad ah u kordhay; 750 ℃ dhumucda lakabka decarburization waxay gaartaa qiimaha ugu badan, waqtigan, hadhuudhka ferrite waa cad yahay, qalafsanaan; marka heerkulku kor u kaco ilaa 800 ℃, dhumucda lakabka decarburization wuxuu bilaabay inuu si weyn hoos ugu dhaco, dhumucdiisuna waxay ku dhacday nus ka mid ah 750 ℃; marka heerkulku sii socdo inuu kor u kaco ilaa 850 ℃ iyo dhumucda decarburization lagu muujiyay sawirka 1. 800 ℃, dhumucdiisuna waxay ka buuxaan lakabka decarburization bilaabay hoos u weyn, dhumucdiisuna waxay ku dhacday 750 ℃ marka kala badh; marka heerkulku sii socdo in uu kor u kaco ilaa 850 ℃ iyo wixii ka sareeya, birta tijaabada dhumucda lakabka decarburization buuxa ayaa sii socota inay hoos u dhacdo, dhumucda lakabka decarburization badhkeed ayaa bilaabay inuu si tartiib tartiib ah u kordhiyo ilaa morphology lakabka decarburization buuxa oo dhan la waayay, lakabka decarburization morphology si tartiib tartiib ah u cad. Waxaa la arki karaa in dhumucda lakabka si buuxda loo gooyay oo leh kororka heerkulka marka hore la kordhiyay ka dibna la dhimay, sababta dhacdadani waxay sabab u tahay muunada habka kuleylka isla mar ahaantaana oxidation iyo decarburization dhaqanka, kaliya marka heerka decarburization waa ka dhaqso badan yahay xawaaraha oksaydhisku waxay u muuqan doontaa ifafaale decarburization. Bilowga kuleyliyaha, dhumucda lakabka si buuxda loo gooyay ayaa si tartiib tartiib ah u kordheysa kororka heerkulka ilaa dhumucda lakabka si buuxda loo gooyay uu gaaro qiimaha ugu sarreeya, waqtigan si loo sii wado kor u qaadista heerkulka, qiyaasta oksidida saamiga ayaa ka dhakhso badan. heerka decarburization-ka, kaas oo xakameynaya kororka lakabka si buuxda loo jaray, taasoo keentay hoos u dhac. Waxaa la arki karaa in, inta u dhaxaysa 675 ℃ 950 ℃, qiimaha dhumucda lakabka si buuxda decarburized at 750 ℃ waa tan ugu weyn, iyo qiimaha dhumucda lakabka si buuxda decarburized at 850 ℃ waa ugu yar. Sidaa darteed, heerkulka kulaylka ee birta tijaabada waxaa lagula talinayaa in ay ahaato 850 ℃.
Jaantus.1 Histomorphology ee lakabka la gooyey ee birta tijaabada ah ee lagu hayo kulaylka kala duwan 1 saac
Marka la barbardhigo lakabka semi-decarburized, dhumucda lakabka si buuxda loo gooyay ayaa saameyn xun oo xun ku leh sifooyinka alaabta, waxay si weyn u yareyn doontaa sifooyinka farsamada ee walxaha, sida hoos u dhigista xoogga, adkaanta, xirashada caabbinta iyo xadka daalka. iwm, iyo sidoo kale kordhinta dareenka dildilaaca, saameeya tayada alxanka iyo wixii la mid ah. Sidaa darteed, xakamaynta dhumucda lakabka si buuxda loo jarjaray ayaa muhiimad weyn u leh hagaajinta waxqabadka alaabta. Jaantuska 2 wuxuu muujinayaa qalooca kala duwanaanshaha dhumucda lakabka si buuxda loo gooyay oo leh heerkul, taas oo muujinaysa kala duwanaanshaha dhumucda lakabka si buuxda loo jarjaray si cad. Waxaa laga arki karaa shaxanka in dhumucda lakabka si buuxda loo gooyay uu yahay kaliya 34μm at 700 ℃; iyada oo heerkulku kor u kaco ilaa 725 ℃, dhumucda lakabka si buuxda loo gooyay ayaa si aad ah u kordheysa ilaa 86 μm, taas oo ka badan laba jeer dhumucda lakabka si buuxda loo gooyey ee 700 ℃; marka heerkulku kor u kaco ilaa 750 ℃, dhumucda lakabka si buuxda loo gooyey Marka heerkulku kor u kaco ilaa 750℃, dhumucda lakabka si buuxda loo gooyey wuxuu gaarayaa qiimaha ugu badan ee 120 μm; Marka heerkulku sii kordho, dhumucda lakabka si buuxda loo gooyay wuxuu bilaabaa inuu si aad ah hoos ugu dhaco, ilaa 70 μm at 800 ℃, ka dibna qiimaha ugu yar ee ku saabsan 20μm at 850 ℃.
Jaantuska.2 Dhumucda lakabka si buuxda u gubtay ee heerkul kala duwan
Saamaynta decarburization ee waxqabadka daalka ee leexinta lafdhabarta
Si loo daraaseeyo saamaynta decarburization ee sifooyinka daalka ee birta guga, laba kooxood oo ka mid ah tijaabooyinka daalka foorarsiga ayaa la sameeyay, kooxdii ugu horreysay waxay ahayd tijaabinta daalka si toos ah iyada oo aan la gooyn, kooxda labaadna waxay ahayd tijaabinta daalka ka dib decarburization isla walaaca. heerka (810 MPa), iyo habka decarburization lagu qabtay 700-850 ℃ 1 saac. Kooxda koowaad ee muunadaha waxa lagu muujiyay shaxda 2, taas oo ah nolosha daalka ee birta guga.
Nolosha daalka ee kooxda koowaad ee shaybaarada ayaa lagu muujiyay shaxda 2. Sida laga arki karo shaxda 2, iyada oo aan la jarin, birta tijaabada ayaa kaliya lagu sameeyay wareegyada 107 ee 810 MPa, mana dhicin wax jab ah; markii heerka walaaca uu dhaafo 830 MPa, qaar ka mid ah shaybaarada ayaa bilaabay inay jabaan; markii heerka walbahaarka uu dhaafo 850 MPa, muunadaha daalka ayaa dhamaantood jabay.
Shaxda 2 Nolosha daalka ee hoos yimaada heerarka walbahaarka kala duwan (iyada oo aan la jarin)
Si loo go'aamiyo xadka daalka, habka kooxda ayaa loo isticmaalaa si loo go'aamiyo xadka daalka ee birta tijaabada, iyo ka dib falanqaynta tirakoobka ee xogta, xadka daalka ee birta tijaabada waa qiyaastii 760 MPa; Si loo tilmaamo nolosha daalka ee birta tijaabada ah ee ku jira cadaadisyo kala duwan, qalooca SN ayaa la sawiray, sida ku cad sawirka 3. Sida laga arki karo sawirka 3, heerarka walaaca kala duwan waxay u dhigmaan nolosha daalka kala duwan, marka nolosha daalka ee 7 , oo u dhiganta tirada wareegyada 107, taas oo macnaheedu yahay in shaybaarka xaaladahan ay ku jiraan gobolka, qiimaha cadaadiska u dhigma waxaa lagu qiyaasi karaa qiimaha xoogga daalka, taas oo ah, 760 MPa. Waxaa la arki karaa in S - N qalooca ay muhiim u tahay go'aaminta nolosha daalka ee maaddadu waxay leedahay qiime tixraac muhiim ah.
Jaantuska 3 SN qalooca tijaabada daal laabashada birta tijaabada ah
Nolosha daalka ee kooxda labaad ee muunadyada ayaa lagu muujiyay shaxda 3. Sida laga arki karo shaxda 3, ka dib markii birta tijaabada lagu gooyo heerkul kala duwan, tirada wareegyada ayaa si cad loo dhimay, waxayna ka badan yihiin 107, iyo dhammaan shaybaarrada daalka ayaa jabay, daalka noloshana si weyn ayaa loo dhimay. Marka lagu daro dhumucda lakabka sare ee la gooyey oo leh qalooca isbeddelka heerkulka ayaa la arki karaa, 750 ℃ dhumucda lakabka la gooyey ayaa ah tan ugu weyn, una dhiganta qiimaha ugu hooseeya ee nolosha daalka. 850 ℃ dhumucda lakabka la gooyey ayaa ah tan ugu yar, oo u dhiganta qiimaha nolosha daalka ayaa aad u sarreeya. Waxaa la arki karaa in dabeecadda decarburization ay si weyn u yareyso waxqabadka daalka ee maaddada, iyo lakabka dhumucdiisuna waxay hoos u dhigtaa nolosha daalka.
Shaxda 3 Nolol daal ah oo heerkulkeedu kala duwan yahay (560 MPa)
Jaantuska jabka daalka ee shaybaarka ayaa lagu arkay iyadoo la baarayo mikroskoob elektaroonig ah, sida ku cad sawirka 4 daalka, waxaa la arki karaa, isha dillaaca ee "kalluunka-isha" non-metallic inclusions, inclusions at fudud si ay u keenaan diiradda stress, taasoo keentay in dildilaaca daal; Jaantuska 4(b) ee qaabka fidinta dildilaaca, waxa la arki karaa xariijimo daal oo cad, oo u qaybsan webiga oo kale, waxa iska leh jabka laxaadka leh, dildilaacaduna sii fidayaan, aakhirkana keena jab. Jaantuska 4 (b) wuxuu muujinayaa qaab-dhismeedka aagga ballaadhinta dillaaca, daal cad oo daal ah ayaa la arki karaa, qaabka qaybinta webiga oo kale, kaas oo ka tirsan jabka quasi-dissociative, iyo ballaarinta joogtada ah ee dildilaaca, ugu dambeyntii keenta jabka. .
Falanqaynta jabka daalka
Jaantus.4 SEM morphology ee daalka jabka dusha sare ee birta tijaabada ah
Si loo go'aamiyo nooca ka mid ahaanshaha sawirka 4, falanqaynta halabuurka tamarta tamarta ayaa la sameeyay, natiijadiina waxaa lagu muujiyay sawirka 5. Waxaa la arki karaa in kuwa aan biraha ahayn ay yihiin inta badan Al2O3, taas oo muujinaysa in ka mid noqoshada waa isha ugu weyn ee dildilaaca ay sababto inclusions dildilaaca.
Jaantuska 5 Spectroscopy Tamarta ee Ku Darida Aan Birta Ahayn
Gabagabo
(1) Dhigista heerkulka kulaylka 850 ℃ waxay yaraynaysaa dhumucda lakabka la gooyey si loo yareeyo saamaynta waxqabadka daalka.
(2) Xadka daalka ee foorarsiga birta tijaabada ah waa 760 MPa.
(3) Tijaabada birta ee dildilaaca ee ka mid ah kuwa aan birta ahayn, badiyaa isku dhafka Al2O3.
( 4) Decarburization si dhab ah u yaraynaysaa nolosha daalka ee birta tijaabada, qaro weyn lakabka decarburization, hoos nolosha daalka.